XF - 8601
| Product and Usage Characteristics | XXC - FR - 8600 | XXC - FR - 8601 | XXC - FR - 8602 | XXC - FR - 8610 |
| Phosphorus Content % | ≥10 | ≥10 | ≥10 | ≥15 |
| Nitrogen Content % | ≥20 | ≥20 | ≥20 | ≥20 |
| Volatile Matter % | ≤0.3 | ≤0.3 | ≤0.3 | ≤0.3 |
| Relative Density g/cm³ | ≤1.3 | ≤1.2 | ≤1.3 | ≤1.2 |
| Average Particle Size (μm) | ≤6 | ≤10 | ≤6 | ≤10 |
| Thermal Decomposition Temperature °C | ≥300 | ≥280 | ≥300 | ≥280 |
| Recommended Extrusion Temperature °C | ≤210 | ≤210 | ≤210 | ≤220 |
| Applicability | TPE (PPO) | TPU (Polyether) | TPE (PPO) | TPE (Non - PPO) |
The processing temperature should be appropriate to avoid the decomposition of the flame retardant due to high temperature. Although the thermal decomposition temperature of this product is greater than 280°C, due to the high shear heat of the screw, if the set screw temperature is too high, the heat - superposition effect caused by heating and shearing is likely to occur, resulting in local overheating of the screw and decomposition of the flame retardant.
| Recommended Addition % | XXC - FR - 8600 | XXC - FR - 8601 | XXC - FR - 8602 | XXC - FR - 8610 |
| TPU 1.6mm V - 0 | / | 30 | / | 30 |
| TPE Medium - V - 1 | 30 | / | 30 | 30 |
- This product should be stored in a cool and dry place. Use it as soon as possible if the packaging is damaged.
- If the packaging is broken or damp, dry it at 100°C ± 10°C for 2 hours before use.
- The above technical parameters are for reference. The actual technical parameters shall be subject to the factory COA or technical agreement.
- The data and information in the application guide and cases are for reference only and shall not be used as product quality standards.